超薄铁基纳米晶带材

超薄铁基纳米晶带材是采用超快速冷却凝固技术制备的铁基软磁合金材料，冷却速度约为106℃/s，厚度为12~27微米，宽度为1~60mm。与传统材料相比，它具有高饱和磁感应强度、高导磁率、低损耗等优良的金属特性，被广泛应用于电力、工业电源、新能源汽车及充电桩、轨道交通、消费电子、无线充电等领域。

分类：

非晶纳米晶带材

咨询电话：+86-18925160436

现在咨询

联系我们

产品详情

超薄铁基纳米晶带材 Super Thin Fe-based Nanocrystalline Ribbons

铁基纳米晶是采用冷却速度大约10⁶°C/S的超急冷凝固技术制备而成的铁基软磁合金材料，厚度有12~27微米，宽度1~60mm，与传统材料相比，具有高饱和磁感、高磁导率，低损耗等优良金属特性，广泛应用于电力电气，工业电源、新能源汽车及充电桩、轨道交通、消费电子、无线充电等领域。

Fe-based nanocrystalline is an fe-based soft magnetic alloy material prepared by ultra-rapid cooling solidification technology with a cooling rate of about 10⁶°C/s, the thickness is 12~27 microns and the width is 1~60mm. Compared with traditional materials, it has excellent metal characteristics such as high saturation magnetic induction, high permeability and low loss, and it's widely used in electric power, industrial power supply, new energy vehicles and charging piles, rail transit, consumer electronics, wireless charging and other fields.

经典应用 Typical Application：

共模滤波电感

EMC Common Mode Choke

中高频功率变压器

Medium and High Frequency Power Transformer

电流互感器（零序、漏保）

Current Transformer CT(Zero Sequence, Leakage Protection)

磁放大器、尖峰抑制器、饱和电感

Magnetic ampliﬁer, Peak Suppressor, Saturated Inductance

无线充电隔磁片

Wireless Charging Electromagnetic Shielding Foil

1K107B 纳米晶薄带性能 Performance of 1K107B Nanocrystalline Ribbon

项目 Item	性能指标（参考值） Performance (Reference)	项目 Item	性能指标（参考值） Performance (Reference)
饱和磁感应强度 Bs(T) Saturation Induction	1.2	密度 ρ(g/cm³) Density	7.3
居里温度 Tc(°C) Curie Temperature	570	电阻率 (μΩ·cm) Resistivity	130
晶化温度 Tx(°C) Crystallization Temperature	515	矫顽力 Hc(A/m) Coercivity	<20
硬度 (Hv) Hardness	880	铁芯填充系数(K) Core Filling Coefficient	>0.78
带材厚度 (μm) Thickness	12~27	铁损 P20kHz/0.5T (W/kg) Core Loss	<20
磁致伸缩系数 (λs) Magnetostriction	2.0X10⁶	铁损 P100kHz/0.3T(W/kg) Core Loss	80